Dr Marco VERITÀ, Stazione Sperimentale del Vetro, Venice (Italy)
Italian window glass chemical composition from the Roman time to the 18th century
Table 3 – Venice, 17th-18th centuries:
composition in wt% of the oxides of window glass fragments.
| sample | colour | dating | SiO2 | Al2O3 | Na2O | K2O | CaO | MgO | SO3 | P2O5 | Cl | TiO2 | Fe2O3 | MnO |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| SL-A | natural | 17th | 69,3 | 1,45 | 12,2 | 4,40 | 8,8 | 1,60 | 0,10 | 0,55 | 1,00 | 0,05 | 0,55 | 0,05 |
| SL-B | natural | 17th | 68,0 | 1,50 | 12,2 | 4,80 | 8,9 | 1,50 | 0,15 | 0,63 | 0,95 | 0,06 | 0,60 | 0,50 |
| Shipwreck | natural | 17th | 65,0 | 1,75 | 11,6 | 4,00 | 11,8 | 3,20 | 0,27 | 0,25 | 0,78 | 0,12 | 0,80 | 0,40 |
| MV1 | colourless | 17th | 65,3 | 1,00 | 14,2 | 2,80 | 9,6 | 4,25 | 0,23 | 0,27 | 0,78 | 0,04 | 0,45 | 0,97 |
| MV2 | colourless | 17th | 66,1 | 1,30 | 12,7 | 2,50 | 10,0 | 4,50 | 0,20 | 0,25 | 0,71 | 0,05 | 0,62 | 1,00 |
| Don1 | colourless | 17th | 66,0 | 1,35 | 13,1 | 6,20 | 7,9 | 2,70 | 0,20 | 0,27 | 0,85 | 0,05 | 0,65 | 0,70 |
| Don2 | colourless | 17th | 68,3 | 1,25 | 13,5 | 4,40 | 7,6 | 2,80 | 0,20 | 0,25 | 0,95 | 0,05 | 0,35 | 0,30 |
| BL2v | natural | 18th | 67,2 | 1,70 | 12,5 | 4,45 | 9,3 | 1,68 | 0,09 | 0,57 | 1,05 | 0,10 | 1,00 | 0,25 |
| BL4v | colourless | 18th | 65,2 | 1,10 | 11,6 | 6,90 | 10,2 | 1,50 | 0,06 | 0,90 | 0,90 | 0,16 | 0,58 | 0,88 |
| BL7v1 | Green | 18th | 60,5 | 2,20 | 12,0 | 4,10 | 14,0 | 3,40 | 0,13 | 1,30 | 0,90 | 0,11 | 1,00 | 0,33 |